Polymaker Fiberon™ PA612-CF15 / black/
Coming soon!
High-performance material
Fiberon™ PA612-CF15 is a carbon fiber reinforced long-chain filament. Due to its chemical structure, this product has lower moisture sensitivity compared to PA6/66 and PA6 based materials and better mechanical properties than PA12 based materials. Additionally, the carbon fiber reinforcement and Warpfree™ technology enhance the dimensional stability of parts produced with this material.
High-performance material
Fiberon™ PA612-CF15 is a carbon fiber reinforced long-chain filament. Due to its chemical structure, this product has lower moisture sensitivity compared to PA6/66 and PA6 based materials and better mechanical properties than PA12 based materials. Additionally, the carbon fiber reinforcement and Warpfree™ technology enhance the dimensional stability of parts produced with this material.
DESCRIPTION
Fiberon™ PA612-CF15 has the same great formula as PolyMide PA612-CF, although Fiberon™ PA612-CF15 may print with a slightly darker shade of black than its predecessor.
Printing, drying, and curing settings?
Printing temperature: 250˚C - 300˚C
Temperature on the work surface: 40˚C - 50˚C
Temperature in the chamber: Room temperature
Print speed: up to 300 mm/s
Cooling fan: OFF
Direct Drive:
Retraction Distance: 3mm
Retraction Speed: 40mm/s
Indirect Drive:
Retraction Distance: 6mm
Retraction Speed: 60mm/s
Recommended drying settings:
Standard drying: 100˚C for 10 hours
PolyDryer: Level 3 for 18 hours (PolyDryer™)
(Only if the material has absorbed moisture)
Hardening settings: 100˚ for 16 hours
Printing, drying, and curing settings?
Printing temperature: 250˚C - 300˚C
Temperature on the work surface: 40˚C - 50˚C
Temperature in the chamber: Room temperature
Print speed: up to 300 mm/s
Cooling fan: OFF
Direct Drive:
Retraction Distance: 3mm
Retraction Speed: 40mm/s
Indirect Drive:
Retraction Distance: 6mm
Retraction Speed: 60mm/s
Recommended drying settings:
Standard drying: 100˚C for 10 hours
PolyDryer: Level 3 for 18 hours (PolyDryer™)
(Only if the material has absorbed moisture)
Hardening settings: 100˚ for 16 hours